1.6mm E308LT0-3 Flux Core Welding Stainless Steel Wire

Product Categories

ER70S-6 [23]
ER70S-G [6]
ER70S-3 [5]
H08A(AWS EL8) [5]
H08Mn(AWS EM12) [6]
H10Mn2(AWS EH14) [5]
ER49-1 [10]
Tungsten Electrodes [2]
ER1100 [5]
ER4043 [10]
ER5356 [8]
ER5556 [4]
ER304 [5]
ER308 [5]
ER309 [6]
ER316 [5]
ER321 [5]
ER90S-G [6]
ER100S-G [1]
WL15 [1]
WL20 [1]
WT20 Tungsten [1]
WC20 [1]
E71T-11 [1]
E71T-GS [1]
E71T-1C [1]
E71T-1C-J [1]
E71T-5C [1]
E70C-6M [1]
E308LT0-3 [1]
E316LT0-3 [1]
E308LT1-1 [1]
E309LT1-1 [1]
E316LT1-1 [1]

Hainan Chenxiang New Material Technology Co., Ltd.

Trust Seal

Verified Supplier

Credit Check

Supplier Assessment

Contact Now

1.6mm E308LT0-3 Flux Core Welding Stainless Steel Wire

Name: 16mm E308LT03 Flux Core Welding Stainless Steel Wire
Brand: CHENXIANG
Price: 1 USD

Buy cheap 1.6mm E308LT0-3 Flux Core Welding Stainless Steel Wire product

Brand Name : CHENXIANG

Model Number : E308LT0-3

Place of Origin : Shandong, China

MOQ : 1000 kilograms

Payment Terms : T/T,L/C

Delivery Time : 5-10 days

Packaging Details : 1kg/5kg/12.5kg spool

Warranty : 3 years

Customized Support : OEM, ODM, OBM

Diameter : 0.8/0.9/1.0/1.2/1.6mm

Melting Point : Standards

Weight : 1kg/5kg/12.5kg

Flux Content : Standards

Sample : Available

Standard : AWS A 5.22

C : 0.022

Si : 0.38

Cu : 0.3

Mn : 1.09

P : 0.017

S : 0.002

Contact Now

1.6mm E308LT0-3 Flux Core Welding Stainless Steel Wire

Product Description

‌E308LT0-3 flux-cored wire is a welding material designed for stainless steel welding, mainly used for welding austenitic stainless steel, such as 304 stainless steel. It has excellent resistance to intergranular corrosion, is suitable for surface surfacing with low requirements, and can be welded with ferrous materials‌‌.

1. Features and Applications

High-efficiency welding‌: Due to its self-protected flux core design, it does not require external gas protection and is easy to operate‌. ‌

Good wind resistance‌: Suitable for use in windy environments, reducing interference during welding‌. ‌

Wide range of application‌: Especially suitable for welding of stainless steel thin plate structures, especially in occasions where the working temperature is below 300℃, it shows good mechanical properties and corrosion resistance‌. 

2. Composition and performance 

Fluoride component‌: The fluoride in the flux core has an important influence on welding spatter. Mixed fluorides (such as sodium fluoride, magnesium fluoride, barium fluoride, and calcium fluoride mixed in a ratio of 1:1:2:6) can effectively reduce welding spatter‌. ‌ 

Oxide surface tension‌: The increase in oxide surface tension will first reduce the welding spatter rate, but too high will increase it. When the surface tension is (330-340)×10^(-7) J/cm^2, the spatter rate is the lowest‌.

Details Images

Standard/Grade	AWS A 5.22 ‌E308LT0-3
Diameter	0.8/0.9/1.0/1.2/1.6mm
Weight	1kg/5kg/12.5kg

1.6mm E308LT0-3 Flux Core Welding Stainless Steel Wire

Specifications

Chemical Composition
C	Si

Product Tags:

308 stainless steel flux core wire

1.6mm flux core welding stainless steel

1.6mm E308LT0-3 Flux Core Welding Stainless Steel Wire Images

Inquiry Cart 0

Send your message to this supplier


*From:	Your email address is incorrect!
*To:	Hainan Chenxiang New Material Technology Co., Ltd.
*Subject:	Subject is empty!
*Message:	For the best results, we recommend including the following details: -Self introduction -Required specifications -Inquire about price/MOQ Characters Remaining: (0/3000) Please enter 20 to 3000 characters to contact this supplier!